Developmental and Reproductive Effects of Iron Oxide Nanoparticles in Arabidopsis thaliana

Increasing use of iron oxide nanoparticles in medicine and environmental remediation has led to concerns regarding exposure of these nanoparticles to the public. However, limited studies are available to evaluate their effects on the environment, in particular on plants and food crops. Here, we investigated the effects of positive (PC) and negative (NC) charged iron oxide (Fe₂O₃) nanoparticles (IONPs) on the physiology and reproductive capacity of Arabidopsis thaliana at concentrations of 3 and 25 mg/L. The 3 mg/L treated plants did not show evident effects on seeding and root length. However, the 25 mg/L treatment resulted in reduced seedling (positive-20% and negative-3.6%) and root (positive-48% and negative-negligible) length. Interestingly, treatment with polyethylenimine (PEI; IONP-PC coating) also resulted in reduced root length (39%) but no change was observed with polyacrylic acid (PAA; IONP-NC coating) treatment alone. However, treatment with IONPs at 3 mg/L did lead to an almost 5% increase in aborted pollen, a 2%–6% reduction in pollen viability and up to an 11% reduction in seed yield depending on the number of treatments. Interestingly, the treated plants did not show any observable phenotypic changes in overall size or general plant structure, indicating that environmental nanoparticle contamination could go dangerously unnoticed.     

水热法一步合成磷酸铁锂及其性能研究

为优化液相法一步制备磷酸铁锂（LiFePO₄）技术,以七水合硫酸亚铁、磷酸二氢铵、一水合氢氧化锂为原料,通过添加十二烷基苯磺酸钠（SDBS）作为表面活性剂,采用液相水热法合成技术,一步合成了LiFePO₄正极材料。研究了水热法一步合成技术对LiFePO₄材料的组成、结构、形貌、粒度等的影响,通过电感耦合等离子体发射光谱仪（ICP-OES）、X射线衍射仪（XRD）、扫描电镜（SEM）、粒度分析仪等对材料进行了表征分析,并测试了材料的电化学性能。研究结果表明,合成得到的LiFePO₄材料为微米级球形颗粒形貌的正交晶系非化学计量比的Li_1.02Fe_0.994PO₄材料。电化学性能测试结果表明,在0.1C倍率下首次充、放电比容量分别为162.0、159.9 mA·h/g,库伦效率达到98.7%、倍率性能（以1C/0.1C保持率计）为92.3%,0.1C倍率循环100次容量保持率为96.4%,展现出良好的电化学性能。     

Mutagenic Effects of Iron Oxide Nanoparticles on Biological Cells

In recent years, there has been an increased interest in the design and use of iron oxide materials with nanoscale dimensions for magnetic, catalytic, biomedical, and electronic applications. The increased manufacture and use of iron oxide nanoparticles (IONPs) in consumer products as well as industrial processes is expected to lead to the unintentional release of IONPs into the environment. The impact of IONPs on the environment and on biological species is not well understood but remains a concern due to the increased chemical reactivity of nanoparticles relative to their bulk counterparts. This review article describes the impact of IONPs on cellular genetic components. The mutagenic impact of IONPs may damage an organism’s ability to develop or reproduce. To date, there has been experimental evidence of IONPs having mutagenic interactions on human cell lines including lymphoblastoids, fibroblasts, microvascular endothelial cells, bone marrow cells, lung epithelial cells, alveolar type II like epithelial cells, bronchial fibroblasts, skin epithelial cells, hepatocytes, cerebral endothelial cells, fibrosarcoma cells, breast carcinoma cells, lung carcinoma cells, and cervix carcinoma cells. Other cell lines including the Chinese hamster ovary cells, mouse fibroblast cells, murine fibroblast cells, Mytilus galloprovincialis sperm cells, mice lung cells, murine alveolar macrophages, mice hepatic and renal tissue cells, and vero cells have also shown mutagenic effects upon exposure to IONPs. We further show the influence of IONPs on microorganisms in the presence and absence of dissolved organic carbon. The results shed light on the transformations IONPs undergo in the environment and the nature of the potential mutagenic impact on biological cells.     

伞帽用高铬铸铁在热强碱腐蚀环境下的磨损分析

针对氧化铝行业中常用的Cr28和Cr20高铬铸铁伞帽在相同工况条件下的磨损机理进行分析,并对比研究了实际生产中两种失效材料的成分、组织及性能。结果表明,伞帽部件在高温强碱腐蚀条件下受到外界冲刷时,磨损量由微切削磨损与变形磨损这两种机制共同决定。含铬量较高的Cr28高铬铸铁,其冲刷和抗腐蚀磨损性能均优于Cr20高铬铸铁。伞帽服役寿命主要受浆料和表层的铸铁材料两大因素影响。两种试验材料经淬火+回火处理后,基体组织中主要为回火马氏体+M₇C₃型碳化物+少量残留奥氏体,其中含铬量较高的Cr28高铬铸铁中共晶碳化物含量更高,且分布更加弥散,其平均硬度值为64.0 HRC,高于Cr20高铬铸铁的60.2 HRC。最终确定Cr28高铬铸铁作为伞帽材质更能满足氧化铝生产及设备检修周期的需要。     

Hierarchical Ni-BDC coated FeOOH nanosheets: A coordination tuning synergistic electrocatalyst with enhanced activity for water oxidation

Hierarchical composites represent a class of efficient electrocatalysts for renewable energy storage and conversion technologies owing to the porous structure and additional exposure of metal sites. Herein, a Ni-based metal organic frameworks (MOFs) (marked as Ni-BDC, BDC stands for 1,4-benzenedicarboxylic acid) nanosheet is successfully fabricated on hydroxyl iron oxide (FeOOH) array with carbon fiber cloth (CFC) as substrate. Benefit from the coordination tuning synergistic effect of the distinct chemical composition and the hierarchical structure for fast mass transportation, the as-obtained FeOOH@Ni-BDC illustrates excellent catalytic ability for electrochemical water oxidation with low overpotential of 270 mV to reach 10 mA/cm² current and good durability in alkaline electrolyte. The novelty of this work lies in the modulation of electronic structure of the FeOOH with Ni-BDC through coordination effect to enhance the activity of the hierarchical composite electrocatalyst. This work is expected to guide the preparation of efficient electrocatalyst for new type alternative energy sources exploitation in near future.     

多元合金化大断面球墨铸铁组织和性能的分析

为了提升大断面球墨铸铁综合力学性能，通过复合添加微量合金元素铜、锑、锡、钼对大断面球墨铸铁进行微合金化处理，借助金相显微镜(OM)、扫描电子显微镜(SEM)及力学性能测试等手段，研究了Cu Sb Sn Mo复合微合金化大断面球墨铸铁微观组织和力学性能。结果表明，试验球墨铸铁具有良好的综合力学性能。大断面球墨铸铁中添加铜、锑、锡、钼后优化了材料的组织结构，基体组织为珠光体＋少量牛眼状铁素体；试样石墨组织细小、圆整，分布均匀。同时，合金元素的复合加入使得其抗拉强度达到800 MPa以上，硬度约为280HB，伸长率达到5%以上。拉伸断口分析表明，微合金化大断面球墨铸铁断裂模式以解理断裂为主，伴有少量的塑性变形。     

酸性废水中As(Ⅲ)、Cu(Ⅱ)与铁粉的反应行为

在Fe-As(Ⅲ)-Cu(Ⅱ)-H₂O体系中, 研究了酸性废水中As(Ⅲ)、Cu(Ⅱ)与金属铁粉的反应行为, 考察了反应过程中As在气、液、固三相中的分配比。结果表明, As(Ⅲ)和Cu(Ⅱ)离子被Fe还原为单质As和Cu后, As、Cu进一步结合成Cu₅As₂等金属间化合物, 从而促进As(Ⅲ)沉淀反应的发生, 且无AsH3生成。在反应时间40min、铁粉过量系数1.2、溶液初始pH=0.0、温度40 ℃、Cu/As摩尔比1.0条件下, As在气、液、固三相中的分配比分别为0、20.7%和79.3%, 沉砷率为79.3%。     

温度对生物净化滤柱中氨氮、铁、锰去除效果的影响

温度是生物净化滤柱运行的一个重要参数，采用生物净化滤柱处理模拟含氨氮、铁、锰地下水，考察水温从约25℃降到约6℃过程中氨氮、铁、锰的去除效果。结果表明，出水氨氮、总铁、锰的浓度分别低于0.15mg/L、0.1mg/L、0.05mg/L，均低于国家标准。出水总铁、锰均未受到水温下降的影响，但是出水氨氮浓度逐渐从约0.02mg/L升高到约0.12mg/L。进一步分析发现，铁主要在滤层的0~0.4m段去除，去除效果没有受到水温变化的影响。氨氮、锰主要在滤层的0~0.8m段去除，其沿程浓度均随水温降低而明显升高。氨氮、锰的生物去除符合一级动力学反应，水温为24.6℃、15.3℃、6.7℃时，两者的动力学常数k分别为0.154min^-1、0.186min^-1，0.143min^-1、0.175min^-1，0.103min^-1、0.163min^-1；半反应时间t_1/2分别为4.51min、3.72min，4.83min、3.96min，6.72min、4.24min。随着试验水温的降低，氨氮、锰的去除效果明显受到影响。     

循环伏安法在润滑油检测中的应用

介绍了循环伏安法的产生背景、原理。应用该技术可以快速、方便地对润滑油中抗氧剂、总酸（碱）值进行测定，并且可以对不同厂家润滑油的抗氧剂包进行区别。该技术还可以有效地评价润滑油的使用寿命和设备工作状况。